Structure, Magnetism, and Thermal Stability of La2NiO2.5F3: A Ruddlesden–Popper Oxyfluoride Crystallizing in Space Group P42/nnm

Authors: J. Jacobs, M.A.L. Marques, H.-C. Wang, E. Dieterich, and S.G. Ebbinghaus

Ref.: Inorg. Chem. 60, 13646-13657 (2021)

Abstract: We report on the new Ruddlesden–Popper (RP) oxyfluoride La2NiO2.5F3 containing an unprecedented high amount of fluorine and Ni2+. This oxyfluoride was prepared by topochemical low-temperature fluorination of La2NiO4, which was obtained by a soft chemistry synthesis, with poly(vinylidene difluoride) (PVDF) as fluorinating agent. La2NiO2.5F3 is the first n = 1 RP compound crystallizing in the tetragonal space group P42/nnm (a = 5.7297(6) Å and c = 13.0106(2) Å). The crystal structure shows a unique tilting scheme of the NiO4F2 octahedra that has so far been only theoretically predicted. Combined neutron and X-ray powder diffraction experiments together with bond-valence-sum and DFT+U calculations reveal an unusual anion ordering with fluoride being located on the apical anion sites of the NiO4F2 octahedra. Excess fluorine ions were found to populate two of the four interstitial anion sites in an ordered fashion. A third interstitial anion position is occupied by oxygen ions while the fourth site remains unoccupied. This hitherto unobserved ordering scenario in RP oxyfluorides promotes a strong layerwise alternating tilting of the NiO4F2 octahedra. Magnetic measurements show strong antiferromagnetic interactions with a high Néel temperature of about 225 K and a pronounced ZFC/FC splitting most likely as the result of a small ferromagnetic moment arising from spin canting. The electronic structure was characterized by DFT and UV–vis spectroscopy, and a strong increase of Eg was found compared to La2NiO4 (3.4 eV vs 1.3 eV).

Citations: 0 (Google scholar)

DOI: 10.1021/acs.inorgchem.1c01957



	doi = {10.1021/acs.inorgchem.1c01957},
	url = {https://doi.org/10.1021%2Facs.inorgchem.1c01957},
	year = 2021,
	month = {aug},
	publisher = {American Chemical Society ({ACS})},
	volume = {60},
	number = {17},
	pages = {13646--13657},
	author = {Jonas Jacobs and Miguel A. L. Marques and Hai-Chen Wang and Emil Dieterich and Stefan G. Ebbinghaus},
	title = {Structure, Magnetism, and Thermal Stability of La$\less$sub$\greater$2$\less$/sub$\greater${NiO}$\less$sub$\greater$2.5$\less$/sub$\greater$F$\less$sub$\greater$3$\less$/sub$\greater$: A Ruddlesden{\textendash}Popper Oxyfluoride Crystallizing in Space Group $\less$i$\greater$P$\less$/i$\greater$4$\less$sub$\greater$2$\less$/sub$\greater$/$\less$i$\greater$nnm$\less$/i$\greater$},
	journal = {Inorganic Chemistry}